Filem PETG Ketahanan Tinggi
Filem PETG Ketahanan Tinggi is a thermoplastic polyester film based on polyethylene terephthalate glycol-modified resin. The glycol modification reduces the crystallization tendency of standard PET, producing an amorphous sheet with higher impact resistance and better thermoforming range. The film is supplied in thicknesses from 0.25 mm to 6.0 mm, in widths up to 2.1 m, with clear, colored, and frosted surface options. Impact strength reaches 8 to 12 kJ/m² by Charpy notched testing, and the film resists crazing under repeated flexural loading. High Durability PETG Film is specified for machine guards, signage, protective barriers, and thermoformed components where optical clarity and impact resistance are required together over a long service period.
Program Filem Tersuai
Filem PETG Ketahanan Tinggi is supplied under an ODM/OEM arrangement. Thickness, width, surface finish, color, and cut format are set according to the buyer's drawing or performance brief. Clear and tinted grades, matte and anti-glare surfaces, and hard-coated variants are developed and documented against a single approved specification sheet, and the approved sheet governs every production lot.
Profil Prestasi
Penyerapan Tenaga Kesan
Filem PETG Ketahanan Tinggi absorbs impact energy through ductile deformation rather than brittle fracture. Charpy notched impact values of 8 to 12 kJ/m² are maintained at temperatures from -20°C to 40°C, so the film retains its protective function in outdoor and cold-storage installations where acrylic sheet cracks.
Rintangan Keletihan Lentur
Struktur amorf filem bertolak ansur dengan lenturan berulang tanpa pemutihan tekanan. Ujian kelesuan lentur kepada ASTM D671 tidak mengembalikan permulaan retak selepas 100,000 kitaran pada amplitud terikan 0.5%, menyokong penggunaan dalam pengadang berengsel, lekapan paparan dan panel penghalang fleksibel.
Kejelasan Optik
Gred jelas bagi Filem PETG Ketahanan Tinggi menghantar 84% hingga 90% cahaya yang boleh dilihat dengan nilai jerebu di bawah 1.0%. Permukaan tidak kuning di bawah pencahayaan dalaman dalam tempoh 10 tahun, dan gred penstabilan UV mengekalkan peralihan warna dalam Delta E 2.0 di bawah 2,000 jam luluhawa dipercepatkan.
Rintangan Kimia dan Pembersihan
Filem ini menentang pembersih alkali cair, detergen neutral dan pembersih berasaskan alkohol. Rintangan kepada pelarut aromatik dan keton adalah terhad; agen pembersih berdasarkan bahan kimia tersebut mengeluarkan gloss permukaan dan dikecualikan daripada protokol penyelenggaraan.
Julat Pembentukan Termo
Filem PETG Ketahanan Tinggi forms at 120°C to 160°C with a wide processing window. Deep draws and complex shapes are produced without pre-drying, and the formed part retains impact resistance at the stretched corners. Mold shrinkage is 0.2% to 0.6%, consistent across production runs.
Kestabilan Dimensi
Filem ini mengekalkan dimensi potongannya merentas perubahan kelembapan daripada 20% hingga 80% kelembapan relatif. Pengembangan haba linear ialah 6.5 x 10⁻⁵ setiap °C, setanding dengan aluminium, yang memudahkan reka bentuk bingkai di mana filem itu dipasang di antara penyemperitan logam.
Data Teknikal
Medan Aplikasi
Soalan Pembeli
Bagaimanakah PETG dibandingkan dengan akrilik untuk aplikasi impak?
Filem PETG Ketahanan Tinggi provides higher impact resistance than cast acrylic at the same thickness, with Charpy notched values of 8 to 12 kJ/m² against typical acrylic values below 2 kJ/m². Acrylic offers higher surface hardness and better scratch resistance. For barrier and guard applications, PETG is specified; for high-scratch display faces, acrylic or a hard-coated PETG grade is preferred.
Adakah pengeringan diperlukan sebelum thermoforming?
Filem PETG Ketahanan Tinggi does not require pre-drying in the normal shop environment. The film absorbs less than 0.2% moisture at 50% relative humidity, and that moisture level does not cause surface defects during forming. If the film has been stored in high humidity for an extended period, a 2-hour dry cycle at 65°C is recommended before forming thick-gauge sheet above 4.0 mm.
Apakah kaedah penamat pemotongan dan tepi yang sesuai?
Filem ini dipotong oleh penghala CNC, laser, gergaji, atau pemotongan mati. Pemotongan laser meninggalkan tepi yang digilap tetapi boleh menghasilkan sedikit warna ambar pada garisan potong; Penghalaan CNC dengan bit seruling tunggal yang tajam menghasilkan kelebihan yang bersih. Menggilap tepi dengan nyalaan atau lap pelarut menghilangkan tanda penghala dan menjelaskan tepi untuk aplikasi yang boleh dilihat.
Bagaimanakah filem itu harus dibersihkan dalam perkhidmatan?
Bersihkan dengan kain lembut dan larutan detergen neutral atau sanitizer berasaskan alkohol. Bilas dengan air bersih dan keringkan dengan kain microfiber. Jangan gunakan pembersih kaca berasaskan ammonia, aseton atau pad yang melelas, yang menyerang permukaan dan mengurangkan kejelasan. Untuk gred bersalut keras, ikut arahan penyelenggaraan pembekal salutan.
Bolehkah filem itu diikat dengan bahan lain?
Filem PETG Ketahanan Tinggi bonds to rigid substrates with solvent-free PU adhesive, acrylic adhesive tape, or structural acrylic adhesive. Solvent-based adhesives containing ketones or aromatic solvents attack the film surface and cause crazing. Test coupon bonding should be completed before production, particularly where the assembly will be exposed to temperature cycling.
Nota Pengendalian dan Penyimpanan
- Simpan kepingan Filem PETG Ketahanan Tinggi rata pada palet tegar di kawasan kering pada suhu 10°C hingga 30°C. Jangan sandarkan cadar pada dinding untuk tempoh yang lama; helaian boleh tunduk di bawah beratnya sendiri.
- Pastikan filem pelekat pelindung di tempatnya semasa pemotongan dan pengendalian untuk mengelakkan calar permukaan. Tanggalkan pelekat dalam masa 30 hari selepas penghantaran untuk mengelakkan pemindahan pelekat ke permukaan filem.
- Bersihkan filem dengan kain lembut dan detergen neutral. Pad pelelas, pembersih berasaskan ammonia dan produk berasaskan pelarut yang mengandungi keton atau aromatik merosakkan permukaan.
- Sokong kawasan lembaran penuh semasa pengangkutan dan pemasangan. Tepi lembaran tolok nipis yang tidak disokong boleh terpesong dan retak apabila diangkat pada satu titik.
- Untuk pemasangan luar, nyatakan gred penstabilan UV dan sahkan sistem penetapan membenarkan pengembangan haba 6.5 x 10⁻⁵ setiap °C tanpa mengekang tepi panel.